Engineering, 24.08.2021 22:20 Ashleymsmith

A steel part, quenched and tempered to a hardness of HRC 45 and then electroplated, is likely to fracture soon after stressing from:

Answers: 2

Show answers

Other questions on the subject: Engineering

Engineering, 04.07.2019 18:10, Fahaddie

The thermal expansion or contraction of a given metal is a function of the f a)-density b)-initial temperature c)- temperature difference d)- linear coefficient of thermal expansion e)- final temperature f)- original length

Answers: 2

continue

Engineering, 04.07.2019 18:10, wyattlb97

Water at the rate of 1 kg/s is forced through a tube with a 2.5 cm inner diameter. the inlet water temperature is 15°c, and the outlet water temperature is 50°c. the tube wall temperature is 14°c higher than the local water temperature all along the length of the tube. what is the length of the tube?

Answers: 3

continue

Engineering, 04.07.2019 19:10, phantomlizz3233

In general, how do thermosetting plastics compare to thermoplastics in mechanical and physical properties?

Answers: 3

continue

Engineering, 06.07.2019 02:30, josediaz1124

Around steel bar, made from material with a yield stress of 750mpa, is loaded so that it has stresses co locations of maximum normal stress and maximum shear stress. use maximum shear stress and maximum distortion energy theories to calculate the safety factors for initial yielding failures.

Answers: 3

continue

You know the right answer?

A steel part, quenched and tempered to a hardness of HRC 45 and then electroplated, is likely to fra...