Engineering, 15.04.2020 18:03 ella9288

A specimen of a 4340 steel alloy with a plane strain fracture toughness K IC = 54.8 MPa m is exposed to a stress of 1030 MPa.

Will this specimen experience fracture if the largest surface crack is 0.5 mm long? Why or why not? Assume that the parameter Y has a value of 1.0.

(b) Will  y , %EL and K IC increase or decrease when

(i) T,
(ii) d/dt,
(iii) grain size increase.

Answers: 2

Show answers

Other questions on the subject: Engineering

Engineering, 04.07.2019 18:10, qwertylol12345

Different types of steels contain different elements that alter the characteristics of the steel. for each of the following elements, explain what the element does when alloyed with steel.

Answers: 2

continue

Engineering, 04.07.2019 18:10, agpraga23ovv65c

Carbon dioxide gas expands isotherm a turbine from 1 mpa, 500 k at 200 kpa. assuming the ideal gas model and neglecting the kinetic and potential energies, determine the change in entropy, heat transfer and work for each kilogram of co2.

Answers: 2

continue

Engineering, 04.07.2019 18:10, Candi9697

A-mn has a cubic structure with a0 0.8931 nm and a density of 7.47 g/cm3. b-mn has a different cubic structure, with a0 0.6326 nm and a density of 7.26 g/cm3. the atomic weight of manganese is 54.938 g/mol and the atomic radius is 0.112 nm. determine the percent volume change that would occur if a-mn transforms to b-mn.

Answers: 2

continue

Engineering, 04.07.2019 18:20, maustin5323

Athin walled concentric tube exchanger is used to cool engine oil from 160°c to 60°c with water that is available at 25°c acting as a coolant. the oil and water flow rates are each at 2 kg/s, and the diameter of the inner tube is 0.5 m and the corresponding value of the overall heat transfer coefficient is 250 w/m2. oc. how long must the heat exchanger be to accomplish the desired cooling? cpwater=4.187 kj/kg-candcpengine el=2.035 kj/kg·°c, oil . 120]

Answers: 1

continue

You know the right answer?

A specimen of a 4340 steel alloy with a plane strain fracture toughness K IC = 54.8 MPa m is exposed...